PHOTOLYSIS OF THE PHENOLIC SOLUTION IN THE PRESENCE OF TiO2 NANOPARTICLES

E.M.Gadirova, I.R.Hasanova, G.S.Aliyeva, G.M.Eyvazova, M.M.Aghayev, Z.O.Gakhramanova*, A.R.Aliyev, H.M.Mahmudov**, M.A.Akhundova, F.M.Muradova

TiO₂nanoparticles have been prepared using sol-gel method from titanium(IV), isopropoxide, isopropyl alcohol, ammonia hydroxide as precursors at mild condition without any post heat treatment for crystallization. The nanocrystalline TiO₂powders were composed of rutile form TiO₂by X-ray diffraction. The size of nanoparticles was examined by transmission electron microscopy and is about 10–15 nm, and the Brunauer-Emmett-Teller specific surface area of the rutile nanopowder makes up 159.6 m²/g. Photochemical degradation of phenol solution under ultraviolet irradiation of the synthesized TiO₂nanoparticles has been carried out

https://doi.org/10.32737/0005-2531-2019-2-52-57

Keywords : nanoTiO2, phenol, photocatalytic process, X-ray diffraction, transmission electron microscopy

View article

SUBMITION

THE LAST NUMBER OF THE JOURNAL

№4 2024

CONTENT

- QUATERNIZATION OF CHITOSAN IN DIFFERENT MEDIA AND IMMOBILIZATION OF DRUGS ON QUATERNIZED CHITOSANH.F.Aslanova, Ch.M.Seidova, S.A.Jabieva, N.T.Shikhverdieva, N.A.Zeynalov, D.B.Tagiyev

- EVALUATION OF THE ANTIOXIDATIVE EFFICACY OF FULLERENE SOOT DOPED BY C60/C70 (85/15) FOR LOW-DENSITY/HIGH PRESSURE POLYETHYLENE NANOCOMPOSITESE.B.Zeynalov, N.S.Allen, M.Ya.Magerramova, A.B.HuseynovMore