STUDY OF LOW-TEMPERATURE OXIDATION OF CARBON MONOOXIDE ON Cu–Mn–Fe CATALYTIC OXIDE SYSTEMS OBTAINED BY THE SOL-GEL COMBUSTION METHOD
G.R.Azimova

The oxidation of carbon monoxide was studied on oxide Cu–Mn–Fe catalytic systems with metal ratio Cu:Mn:Fe=1:1:1; 2:1:1; 1:2:1 and 1:1:2 obtained by the sol-gel method with combustion. The results of X-ray phase analysis showed that the catalytic systems have a complex phase composition. Along with double oxides of manganese and iron, ferrites of copper-, manganese, copper manganite, manganese-substituted copper ferrites were formed (CuFe2O4; Mn0.43Fe2.57O4, Mn0.98Fe2.02O4; CuMn2O4; Cu1.2Mn1.8O4;  Cu0.5Mn0.5Fe2O4). It has been found that depending on the ratio of metals in the catalyst, the reaction start temperature is in the temperature range of 120–1700C. And after 3–5 minutes after the start of the reaction, the conversion begins to increase sharply, reaching 100% within the next 5 minutes

doi.org/10.32737/0005-2531-2022-2-93-99

Keywords : oxidation, carbon monoxide, combustion sol-gel synthesis, oxides, spinels
View article
SUBMITION
THE LAST NUMBER OF THE JOURNAL
№1 2025
CONTENT
- REACTIVITY OF METAL COMPLEXES WITH RADICALSA.A.Medjidov, R.H.Ismayilov, P.A.Fatullayeva, D.B.Tagiyev
- PERSPECTIVES ON THE TECHNICAL, SCIENTIFIC AND PRACTICAL BENEFITS IN THE USE OF SINGLE-PACK STABILISER FORMULATIONS FOR POLYMER PROCESSINGB.Johnson, K.Keck-Antoine, N.S.Allen, M.Edge, S.Hussain, E.ZeynalovMore