THERMOPHYSICAL PROPERTIES OF ALLOY COMPOSITIONS (2Bi2O3∙B2O3)100-x(2Bi2O3∙3GeO2)x (x=0, 10, 50)
S.I.Bananyarli, Sh.S.Ismayilov, R.N.Gasimova, L.A.Khalilova

The termophisical properties, namely, the temperature dependence of thermal conductivity, thermal resistance and heat capacity of the allays compositions (2Bi2O3∙B2O3)100-x (2Bi2O3∙3GeO2)x in the (300–600) K temperature range have ligated been invest. An increase in thermal conductivity χ(T) above 500 K is probably associated with the softening of alloys and the presence of blurred phase transitions, which are accompanied by partial breaking of chemical bonds. It was revealed that the heat capacity in alloys of the compositions (2Bi2O3∙B2O3)100-x (2Bi2O3∙3GeO2)x increases with an increase in the GeO2 concentration. In the studied samples, that showed their own disorder during solidification, the thermal conductivity is strongly reduced due to the enhancement of the anharmonicity of phonon – phonon interactions. İn turn a small "disorder" introduced by defects due to the difference in masses is not noticeable against the background of the huge "disorder" inherent in oxide substances

doi.org/10.32737/0005-2531-2021-3-44-48 

 

Keywords : thermal conductivity, thermal resistance, heat capacity, phonons, germanium oxide, alloys
View article
SUBMITION
THE LAST NUMBER OF THE JOURNAL
№1 2022
CONTENT
- IMMOBILIZATION OF LEVOTHYROXINE IN QUATERNIZED N,N-DIETYL N-METHYL CHITOSAN HYDROGEL AND CHEMICAL NATURE OF THE INTERACTIONS.F.Safaraliyeva, A.F.Hummetov, Sh.Z.Tapdiqov, S.S.Fatullayeva, M.Raucci, D.B.Tagiyev, N.A.Zeynalov
- CATALYTIC OXIDATIVE CONVERSION OF LOWER OLEFINS AND PARAFFINS OVER ZEOLITES MODIFIED WITH DIFFERENT METAL CATIONSA.M.Aliyev, F.V.Aliyev, A.R.Safarov, M.Y.Abbasov, T.I.Guseynova, R.A.Ahmadov, R.Yu.AgayevaMore